Density
(lbs/cubic inch)
|
Thermal Conduct
(BTU/Sq Ft/Hr/° F @ 68° F)
|
Elec. Conductivity
(% IACS @ 68° F Soft)
|
Elec. Resistivity
(10.3 ohms/cmf)
|
Melting Point
(Solidus ° F)
|
|
Certified OFHC Copper CDA10100 ( 99.99% min Cu )
|
|
.323
|
226
|
101
|
10.3
|
1981
|
|
OFHC Copper CDA10200 ( 99.95% min Cu )
|
|
.323
|
226
|
101
|
10.3
|
1981
|
|
ETP Copper CDA11000 ( 99.90% min Cu ; .04% Oxygen )
|
|
.323
|
226
|
101
|
10.3
|
1981
|
|
Zirconium Copper CDA15000 ( 99.85% Cu ; .15% Zr )
|
|
.321
|
212
|
93
|
11.2
|
1796
|
|
Cadmium Copper CDA16200 ( 99% Cu ; 1% Cd )
|
|
.321
|
208
|
90
|
11.5
|
1886
|
|
Beryllium Copper CDA17200 ( 98.1% Cu ; 1.9% Be )
|
|
.302
|
60
|
17
|
46.2
|
1590
|
|
Cd. Cr. Copper CDA18135 ( 99.2% Cu ; .4% Cd ; .4% Cr )
|
|
.323
|
210
|
92
|
11.3
|
1880
|
|
Cartridge Brass CDA26000 ( 70% Cu ; 30% Zn )
|
|
.308
|
70
|
28
|
37.0
|
1880
|
|
Yellow Brass CDA27000 ( 65% Cu ; 35% Zn )
|
|
.306
|
67
|
27
|
38.4
|
1680
|
|
Phosphor Bronze CDA51000 ( 94.8% Cu ; 5% Sn ; .2% P )
|
|
.320
|
40
|
15
|
69.1
|
1750
|
 |
Typical Mechanical Properties (.080")
|
|
Tensile Strength
(1000 lbs. psi )
|
Yield Strength @ 0.05% extension under load
(1000 lbs. psi )
|
Elongation
in 2 inch sample (%)
|
|
Spring
|
Hard
|
Soft .025"
|
Spring
|
Hard
|
Soft .025"
|
Spring
|
Hard
|
Soft .025"
|
|
Certified OFHC Copper CDA10100 ( 99.99% min Cu )
|
|
66
|
55
|
34
|
57
|
50
|
11
|
3
|
6
|
54
|
|
Certified OFHC Copper CDA10200 ( 99.95% min Cu )
|
|
66
|
55
|
34
|
57
|
50
|
11
|
3
|
6
|
53
|
|
Certified OFHC Copper CDA11000 ( 99.90% min Cu ; .04% Oxygen )
|
|
66
|
55
|
34
|
57
|
50
|
12
|
3
|
5
|
42
|
|
Zirconium Copper CDA15000 ( 99.85% Cu ; .15% Zr )
|
|
72*
|
64*
|
30
|
68
|
62
|
13
|
3
|
15
|
49
|
|
Cadmium Copper CDA16200 ( 99% Cu ; 1% Cd )
|
|
80
|
70
|
38
|
66
|
55
|
12
|
3
|
6
|
50
|
|
Beryllium Copper CDA17200 ( 98.1% Cu ; 1.9% Be )
|
|
212
|
152
|
68
|
195
|
125
|
28
|
3
|
1
|
35
|
|
Cd. Cr. Copper CDA18135 ( 99.2% Cu ; .4% Cd ; .4% Cr )
|
|
130
|
110
|
65
|
70
|
60
|
27
|
3
|
8
|
45
|
|
Cartridge Brass CDA26000 ( 70% Cu ; 30% Zn )
|
|
130
|
109
|
52
|
70
|
68
|
21
|
3
|
8
|
58
|
|
Yellow Brass CDA27000 ( 65% Cu ; 35% Zn )
|
|
128
|
108
|
52
|
70
|
67
|
21
|
3
|
5
|
56
|
|
Phosphor Bronze CDA51000 ( 94.8% Cu ; 5% Sn ; .2% P )
|
|
140
|
110
|
51
|
88
|
85
|
21
|
3
|
5
|
56
|
* Solution Heat treat, cold work and aged.
Click here to return to Copper and Copper Alloys Characteristics
|